Cold Forming Plastic Sheet

This is a type of vacuum forming where thin or thick gauge plastic sheet is placed over a die heated to a temperature that allows the material to become pliable then is stretched over the surface of the die while vacuum pressure pulls the sheet down and into its final shape.

Cold forming plastic sheet.

The recommended radius of curvature should be a value greater than 180 times the thickness of the sheet for plexiglas g sheet and 300 times the thickness for plexiglas mc sheet see table below. Our tanks are formed from sheet stock typically 0 25 in. The only major variable that can affect the forming process is the thickness of the plastic sheet. For thicker sheets it will take longer and for thinner sheets it will take less time.

Incomplete part formation detail. I am forming plastic not metal but i am applying metal bending principles to my application after a few years of iteration we have developed an accurate flat pattern method for our tank bending operations. Sheet too hot. Modify the timing as necessary.

Sheet too cold to form heat sheet for longer time period. Cold forming plexiglas sheet can be cold formed bent at room temperature in a smooth arc and held to a radius by forcing the material into a curved channel support. Uk educational supply center centre mindsets online sells variously sized 3mm thick sample sheets of eastman s spectar copolyester at not completely outlandish prices. This article uses a sheet about 1 4 thick so all times are about 10 to 15 minutes per step.

Uneven heating check heaters screen hot areas.